越來越多的鋁板產品的金屬外殼都使用了金屬拉絲工藝，以起到美觀，抗侵蝕的作用。使產品兼備時尚和科技的元素。這也是該工藝備受歡迎的原因之一，今天就跟著鋁板生產廠家來了解一下鋁板表面產生色差的因素有哪些。
More and more metal shells of aluminum plate products use metal wire drawing process to play a role of beauty and corrosion resistance. The product combines fashion and technology elements. This is also one of the reasons why this process is so popular. Today, let's learn about the factors that cause color difference on the aluminum plate surface.
1.染料溶液的溫度：鋁板的染色分為冷染和熱染，冷染在生產過程中長期使用，對顏色均勻性有很好的把握。熱染的使用是短暫的，但很難操縱顏色。熱染色溫度一般在40°C～60°C，如果溫度過高，會減少染色的吸附，使鋁板表面容易開花。
1. Temperature of dye solution: The dyeing of aluminum plate can be divided into cold dyeing and hot dyeing. Cold dyeing is used for a long time in the production process and has a good grasp of color uniformity. The use of hot dyeing is short-lived, but it is difficult to manipulate the color. The thermal dyeing temperature is generally 40 ° C~60 ° C. If the temperature is too high, the adsorption of dyeing will be reduced, making the aluminum plate surface easy to bloom.
2.對于氧化鋁膜單板質量：氧化膜是指鋁單板的厚度，孔隙率，透明度等，鋁板氧化膜厚度可保持在10微米以上，可獲得孔隙率和透明度，可獲得較佳的染色質量。
2. For the quality of aluminum oxide film veneer: the oxide film refers to the thickness, porosity, transparency, etc. of the aluminum veneer. The thickness of the aluminum oxide film can be kept above 10 microns, so that porosity and transparency can be obtained, and better dyeing quality can be obtained.

3.濃度的染色液：染色溶液的濃度和的關系的染色。著色鋁單板，較低的濃度，暗稍高濃度后。如果染料的較高濃度將顏色不均勻或浮色，在洗滌過程中容易地發生，并且在封閉的“彩色流”。為了提高染料的染料吸附能力，使用顏色的低濃度的延長染色時，染料分子滲透到更均勻的氧化膜的孔的深度，并且使顏色更和諧固體。
3. Staining solution of concentration: dyeing of the relationship between the concentration of dyeing solution and. Colored aluminum veneer, low concentration, dark slightly after high concentration. If the higher concentration of dye will cause the color to be uneven or floating, it will easily occur in the washing process, and in the closed "color flow". In order to improve the dye adsorption capacity of the dye, when the low concentration of color is used to extend the dyeing, the dye molecules penetrate into the hole depth of the more uniform oxide film, and make the color more harmonious solid.
4.影響的鋁原料單板部分：一般情況下，高純鋁，鋁鎂，鋁錳合金在生產過程中經過陽極氧化處理后，其染色性能好，可染成多種顏色，對于重硅或銅板，在染色過程中只能染成深色和黑色，顏色較為單調。
4. Affected aluminum raw material veneer: In general, high-purity aluminum, aluminum magnesium, and aluminum manganese alloys have good dyeing performance after anodizing in the production process, and can be dyed into a variety of colors. For heavy silicon or copper plates, they can only be dyed into dark and black during the dyeing process, and the color is relatively monotonous.
現在的鋁板市場上,目前常見的鋁板為了使其產品的表面裝飾性變得更好，如果鋁板的顏色效果不能達到理想的效果，它的應用將產生巨大的影響。所以說在生產使用前后要注重問題的預防，更多相關信息就來我們這里http://www.ahxsxljk.com咨詢吧！
In the current aluminum plate market, in order to make the surface decoration of its products better, if the color effect of aluminum plate can not achieve the desired effect, its application will have a huge impact. So we should pay attention to the prevention of problems before and after production and use. More relevant information will come to us http://www.ahxsxljk.com Consult!